ACRYLITE® Film 0F032 Matt Surface


ACRYLITE® Film 0F032 matt is a very high UV and weather resistant acrylic film with both side matt surfaces for graphic printings and high quality lamination's.

The film maintains high light transmission properties even though it displays a matt surface. Therefore it is suitable to create matt finishing effects even after printing and lamination.

The matt finish provides an anti-blocking effect in printing processes and light scattering can be achieved when used in illumination applications.

The irreversible anti-glare surface of this film is not affected by thermoforming or deep drawing.


ACRYLITE® Film 0F032 matt can be used to be printed on as high quality film decoration and then laminated on different polymeric films and sheets. Laminated decoration films based on ACRYLITE® are suitable for a wide range of molding processes such as thermoforming and insert molding.

In labels, tapes and graphic arts, it can be used as a matt single face layer or matt overlay in laminate systems for high UV and weathering protection.

Due to its good anti-glare and matt surface, it can be used as overlay in high quality ID Cards.


ACRYLITE® Film 0F032 has a good printability behavior in all printing technologies such as gravure, flexography and digital. In most of the cases any pre-treatment or primers are not required.

This film can be laminated onto polymeric substrates such as films or extruded sheets based on PVC, PC, ABS, PMMA and ASA by in-line or roll-to-roll heat lamination.

High quality laminates in between ACRYLITE® Film 0F032 and other polymeric substrates such as PET, PC, PP, PE and PVC can be achieved with pressure sensitive adhesives (PSA) or solvent based adhesives.

The film can be cut-to-size or die cut.

Sales range

It is delivered in standard rolls of 70μm thickness, 1420mm width and 2050mm length.

Tailor made rolls can be produced under prior commercial agreement.

Technical data

PropertiesTest methodUnitValue
Luminous transmittance D65 ISO 13468-2 % 90
UV transmittance (280 – 380 nm) DIN EN 410:2011 % < 1
Gloss (60)° DIN 67530 22
Tensile stress at yield (y) ISO 527-3 MPa 35
Yield strain (εγ) ISO 527-3 % 6
Nominal strain at break (B) ISO 527-3 % > 50
Glass transition temperature Tg (DSC) ISO 11357 ° C 88
Accelerated weathering resistance ISO 4892-2 method A, cycle 1, 65% RH H 12000 No visible change
Specific gravity DIN 53479 g/cm³ 1,13
Surface tension DIN 53364 mN/m 50